Praseodymium

Praseodymium
Hazards
	GHS labelling:
Pictograms
Signal word	Danger
Hazard statements	H250
Precautionary statements	P222, P231, P422
NFPA 704 (fire diamond)	0 4 4

Praseodymium, ₅₉Pr
Praseodymium
Pronunciation	(PRAY-zee-ə-DIM-ee-əm)
Appearance	grayish white
Standard atomic weight Ar°(Pr)
	140.90766±0.00001; 140.91±0.01 (abridged) ;
Praseodymium in the periodic table
	cerium ← praseodymium → neodymium
Atomic number (Z)	59
Group	f-block groups (no number)
Period	period 6
Block	f-block
Electron configuration	[Xe] 4f3 6s2
Electrons per shell	2, 8, 18, 21, 8, 2
Physical properties
Phase at STP	solid
Melting point	1208 K (935 °C, 1715 °F)
Boiling point	3403 K (3130 °C, 5666 °F)
Density (near r.t.)	6.77 g/cm3
when liquid (at m.p.)	6.50 g/cm3
Heat of fusion	6.89 kJ/mol
Heat of vaporization	331 kJ/mol
Molar heat capacity	27.20 J/(mol·K)
Atomic properties
Oxidation states	0, +1, +2, +3, +4, +5 (a mildly basic oxide)
Electronegativity	Pauling scale: 1.13
Ionization energies	1st: 527 kJ/mol ; 2nd: 1020 kJ/mol ; 3rd: 2086 kJ/mol ; ;
Atomic radius	empirical: 182 pm
Covalent radius	203±7 pm
	Spectral lines of praseodymium
Other properties
Natural occurrence	primordial
Crystal structure	double hexagonal close-packed (dhcp)
Speed of sound thin rod	2280 m/s (at 20 °C)
Thermal expansion	α, poly: 6.7 µm/(m⋅K) (at r.t.)
Thermal conductivity	12.5 W/(m⋅K)
Electrical resistivity	α, poly: 0.700 µΩ⋅m (at r.t.)
Magnetic ordering	paramagnetic
Molar magnetic susceptibility	+5010.0×10−6 cm3/mol (293 K)
Young's modulus	α form: 37.3 GPa
Shear modulus	α form: 14.8 GPa
Bulk modulus	α form: 28.8 GPa
Poisson ratio	α form: 0.281
Vickers hardness	250–745 MPa
Brinell hardness	250–640 MPa
CAS Number	7440-10-0
History
Discovery	Carl Auer von Welsbach (1885)
Isotopes of praseodymium
ε	142Ce

Praseodymium is a chemical element; it has symbol Pr and the atomic number 59. It is the third member of the lanthanide series and is considered one of the rare-earth metals. It is a soft, silvery, malleable and ductile metal, valued for its magnetic, electrical, chemical, and optical properties. It is too reactive to be found in native form, and pure praseodymium metal slowly develops a green oxide coating when exposed to air.

Praseodymium always occurs naturally together with the other rare-earth metals. It is the sixth-most abundant rare-earth element and fourth-most abundant lanthanide, making up 9.1 parts per million of the Earth's crust, an abundance similar to that of boron. In 1841, Swedish chemist Carl Gustav Mosander extracted a rare-earth oxide residue he called didymium from a residue he called "lanthana", in turn separated from cerium salts. In 1885, the Austrian chemist Carl Auer von Welsbach separated didymium into two elements that gave salts of different colours, which he named praseodymium and neodymium. The name praseodymium comes from the Ancient Greek πράσινος (prasinos), meaning 'leek-green', and δίδυμος (didymos) 'twin'.

Like most rare-earth elements, praseodymium most readily forms the +3 oxidation state, which is the only stable state in aqueous solution, although the +4 oxidation state is known in some solid compounds and, uniquely among the lanthanides, the +5 oxidation state is attainable in matrix-isolation conditions. The 0, +1, and +2 oxidation states are rarely found. Aqueous praseodymium ions are yellowish-green, and similarly, praseodymium results in various shades of yellow-green when incorporated into glasses. Many of praseodymium's industrial uses involve its ability to filter yellow light from light sources.

Physical properties

Praseodymium is the third member of the lanthanide series, and a member of the rare-earth metals. In the periodic table, it appears between the lanthanides cerium to its left and neodymium to its right, and above the actinide protactinium. It is a ductile metal with a hardness comparable to that of silver. Praseodymium is calculated to have a very large atomic radius; with a radius of 247 pm, barium, rubidium and caesium are larger. However, observationally, it is usually 185 pm. Praseodymium's 59 electrons are arranged in the configuration [Xe]4f³6s²; theoretically, all five outer electrons can act as valence electrons, but the use of all five requires extreme conditions and normally, praseodymium only gives up three or sometimes four electrons in its compounds.

Like most other metals in the lanthanide series, praseodymium usually only uses three electrons as valence electrons, as afterward the remaining 4f electrons are too strongly bound: this is because the 4f orbitals penetrate the most through the inert xenon core of electrons to the nucleus, followed by 5d and 6s, and this increases with higher ionic charge. Praseodymium nevertheless can continue losing a fourth and even occasionally a fifth valence electron because it comes very early in the lanthanide series, where the nuclear charge is still low enough and the 4f subshell energy high enough to allow the removal of further valence electrons. Thus, similarly to the other early trivalent lanthanides, praseodymium has a double hexagonal close-packed crystal structure at room temperature. At about 560 °C, it transitions to a face-centered cubic structure, and a body-centered cubic structure appears shortly before the melting point of 935 °C.

Praseodymium, like all of the lanthanides, is paramagnetic at room temperature. Unlike some other rare-earth metals, which show antiferromagnetic or ferromagnetic ordering at low temperatures, praseodymium is paramagnetic at all temperatures above 1 K.

Chemical properties

Praseodymium metal tarnishes slowly in air, forming a spalling green oxide layer like iron rust; a centimetre-sized sample of praseodymium metal corrodes completely in about a year. It burns readily at 150 °C to form praseodymium(III,IV) oxide, a nonstoichiometric compound approximating to Pr₆O₁₁:

12 Pr + 11 O₂ → 2 Pr₆O₁₁

This may be reduced to praseodymium(III) oxide (Pr₂O₃) with hydrogen gas. Praseodymium(IV) oxide, PrO₂, is the most oxidised product of the combustion of praseodymium and can be obtained by either reaction of praseodymium metal with pure oxygen at 400 °C and 282 bar or by disproportionation of Pr₆O₁₁ in boiling acetic acid. The reactivity of praseodymium conforms to periodic trends, as it is one of the first and thus one of the largest lanthanides. At 1000 °C, many praseodymium oxides with composition PrO_2−x exist as disordered, nonstoichiometric phases with 0 < x < 0.25, but at 400–700 °C the oxide defects are instead ordered, creating phases of the general formula Pr_nO_2n−2 with n = 4, 7, 9, 10, 11, 12, and ∞. These phases PrO_y are sometimes labelled α and β′ (nonstoichiometric), β (y = 1.833), δ (1.818), ε (1.8), ζ (1.778), ι (1.714), θ, and σ.

Praseodymium is an electropositive element and reacts slowly with cold water and quite quickly with hot water to form praseodymium(III) hydroxide:

2 Pr (s) + 6 H₂O (l) → 2 Pr(OH)₃ (aq) + 3 H₂ (g)

Praseodymium metal reacts with all the stable halogens to form trihalides:

2 Pr (s) + 3 F₂ (g) → 2 PrF₃ (s) [green]

2 Pr (s) + 3 Cl₂ (g) → 2 PrCl₃ (s) [green]

2 Pr (s) + 3 Br₂ (g) → 2 PrBr₃ (s) [green]

2 Pr (s) + 3 I₂ (g) → 2 PrI₃ (s)

The tetrafluoride, PrF₄, is also known, and is produced by reacting a mixture of sodium fluoride and praseodymium(III) fluoride with fluorine gas, producing Na₂PrF₆, following which sodium fluoride is removed from the reaction mixture with liquid hydrogen fluoride. Additionally, praseodymium forms a bronze diiodide; like the diiodides of lanthanum, cerium, and gadolinium, it is a praseodymium(III) electride compound.

Praseodymium dissolves readily in dilute sulfuric acid to form solutions containing the chartreuse Pr³⁺ ions, which exist as [Pr(H₂O)₉]³⁺ complexes:

2 Pr (s) + 3 H₂SO₄ (aq) → 2 Pr³⁺ (aq) + 3 SO²⁻
₄ (aq) + 3 H₂ (g)

Dissolving praseodymium(IV) compounds in water does not result in solutions containing the yellow Pr⁴⁺ ions; because of the high positive standard reduction potential of the Pr⁴⁺/Pr³⁺ couple at +3.2 V, these ions are unstable in aqueous solution, oxidising water and being reduced to Pr³⁺. The value for the Pr³⁺/Pr couple is −2.35 V. However, in highly basic aqueous media, Pr⁴⁺ ions can be generated by oxidation with ozone.

Although praseodymium(V) in the bulk state is unknown, the existence of praseodymium in its +5 oxidation state (with the stable electron configuration of the preceding noble gas xenon) under noble-gas matrix isolation conditions was reported in 2016. The species assigned to the +5 state were identified as [PrO₂]⁺, its O₂ and Ar adducts, and PrO₂(η²-O₂).

Organopraseodymium compounds

Organopraseodymium compounds are very similar to those of the other lanthanides, as they all share an inability to undergo π backbonding. They are thus mostly restricted to the mostly ionic cyclopentadienides (isostructural with those of lanthanum) and the σ-bonded simple alkyls and aryls, some of which may be polymeric. The coordination chemistry of praseodymium is largely that of the large, electropositive Pr³⁺ ion, and is thus largely similar to those of the other early lanthanides La³⁺, Ce³⁺, and Nd³⁺. For instance, like lanthanum, cerium, and neodymium, praseodymium nitrates form both 4:3 and 1:1 complexes with 18-crown-6, whereas the middle lanthanides from promethium to gadolinium can only form the 4:3 complex and the later lanthanides from terbium to lutetium cannot successfully coordinate to all the ligands. Such praseodymium complexes have high but uncertain coordination numbers and poorly defined stereochemistry, with exceptions resulting from exceptionally bulky ligands such as the tricoordinate [Pr{N(SiMe₃)₂}₃]. There are also a few mixed oxides and fluorides involving praseodymium(IV), but it does not have an appreciable coordination chemistry in this oxidation state like its neighbour cerium. However, the first example of a molecular complex of praseodymium(IV) has recently been reported.

Isotopes

Praseodymium has only one stable and naturally occurring isotope, ¹⁴¹Pr. It is thus a mononuclidic and monoisotopic element, and its standard atomic weight can be determined with high precision as it is a constant of nature. This isotope has 82 neutrons, which is a magic number that confers additional stability. This isotope is produced in stars through the s- and r-processes (slow and rapid neutron capture, respectively). Thirty-eight other radioisotopes have been synthesized. All of these isotopes have half-lives under a day (and most under a minute), with the single exception of ¹⁴³Pr with a half-life of 13.6 days. Both ¹⁴³Pr and ¹⁴¹Pr occur as fission products of uranium. The primary decay mode of isotopes lighter than ¹⁴¹Pr is positron emission or electron capture to isotopes of cerium, while that of heavier isotopes is beta decay to isotopes of neodymium.

History

In 1751, the Swedish mineralogist Axel Fredrik Cronstedt discovered a heavy mineral from the mine at Bastnäs, later named cerite. Thirty years later, the fifteen-year-old Wilhelm Hisinger, from the family owning the mine, sent a sample of it to Carl Scheele, who did not find any new elements within. In 1803, after Hisinger had become an ironmaster, he returned to the mineral with Jöns Jacob Berzelius and isolated a new oxide, which they named ceria after the dwarf planet Ceres, which had been discovered two years earlier. Ceria was simultaneously and independently isolated in Germany by Martin Heinrich Klaproth. Between 1839 and 1843, ceria was shown to be a mixture of oxides by the Swedish surgeon and chemist Carl Gustaf Mosander, who lived in the same house as Berzelius; he separated out two other oxides, which he named lanthana and didymia. He partially decomposed a sample of cerium nitrate by roasting it in air and then treating the resulting oxide with dilute nitric acid. The metals that formed these oxides were thus named lanthanum and didymium.

While lanthanum turned out to be a pure element, didymium was not and turned out to be only a mixture of all the stable early lanthanides from praseodymium to europium, as had been suspected by Marc Delafontaine after spectroscopic analysis, though he lacked the time to pursue its separation into its constituents. The heavy pair of samarium and europium were only removed in 1879 by Paul-Émile Lecoq de Boisbaudran and it was not until 1885 that Carl Auer von Welsbach separated didymium into praseodymium and neodymium. Von Welsbach confirmed the separation by spectroscopic analysis, but the products were of relatively low purity. Since neodymium was a larger constituent of didymium than praseodymium, it kept the old name with disambiguation, while praseodymium was distinguished by the leek-green colour of its salts (Greek πρασιος, "leek green"). The composite nature of didymium had previously been suggested in 1882 by Bohuslav Brauner, who did not experimentally pursue its separation.

Occurrence and production

Praseodymium is not particularly rare, despite it being in the rare-earth metals, making up 9.2 mg/kg of the Earth's crust. This value is between those of thorium (9.6 mg/kg) and samarium (7.05 mg/kg), and makes praseodymium the fourth-most abundant of the lanthanides, behind cerium (66.5 mg/kg), neodymium (41.5 mg/kg), and lanthanum (39 mg/kg); it is less abundant than the rare-earth elements yttrium (33 mg/kg) and scandium (22 mg/kg). Instead, praseodymium's classification as a rare-earth metal comes from its rarity relative to "common earths" such as lime and magnesia, the few known minerals containing it for which extraction is commercially viable, as well as the length and complexity of extraction. Although not particularly rare, praseodymium is never found as a dominant rare earth in praseodymium-bearing minerals. It is always preceded by cerium and lanthanum and usually also by neodymium.

The Pr³⁺ ion is similar in size to the early lanthanides of the cerium group (those from lanthanum up to samarium and europium) that immediately follow in the periodic table, and hence it tends to occur along with them in phosphate, silicate and carbonate minerals, such as monazite (M^IIIPO₄) and bastnäsite (M^IIICO₃F), where M refers to all the rare-earth metals except scandium and the radioactive promethium (mostly Ce, La, and Y, with somewhat less Nd and Pr). Bastnäsite is usually lacking in thorium and the heavy lanthanides, and the purification of the light lanthanides from it is less involved. The ore, after being crushed and ground, is first treated with hot concentrated sulfuric acid, evolving carbon dioxide, hydrogen fluoride, and silicon tetrafluoride. The product is then dried and leached with water, leaving the early lanthanide ions, including lanthanum, in solution.

The procedure for monazite, which usually contains all the rare earth, as well as thorium, is more involved. Monazite, because of its magnetic properties, can be separated by repeated electromagnetic separation. After separation, it is treated with hot concentrated sulfuric acid to produce water-soluble sulfates of rare earth. The acidic filtrates are partially neutralized with sodium hydroxide to pH 3–4, during which thorium precipitates as hydroxide and is removed. The solution is treated with ammonium oxalate to convert rare earth to their insoluble oxalates, the oxalates are converted to oxides by annealing, and the oxides are dissolved in nitric acid. This last step excludes one of the main components, cerium, whose oxide is insoluble in HNO₃. Care must be taken when handling some of the residues as they contain ²²⁸Ra, the daughter of ²³²Th, which is a strong gamma emitter.

Praseodymium may then be separated from the other lanthanides via ion-exchange chromatography, or by using a solvent such as tributyl phosphate where the solubility of Ln³⁺ increases as the atomic number increases. If ion-exchange chromatography is used, the mixture of lanthanides is loaded into one column of cation-exchange resin and Cu²⁺ or Zn²⁺ or Fe³⁺ is loaded into the other. An aqueous solution of a complexing agent, known as the eluant (usually triammonium edtate), is passed through the columns, and Ln³⁺ is displaced from the first column and redeposited in a compact band at the top of the column before being re-displaced by NH⁺
₄. The Gibbs free energy of formation for Ln(edta·H) complexes increases along with the lanthanides by about one quarter from Ce³⁺ to Lu³⁺, so that the Ln³⁺ cations descend the development column in a band and are fractionated repeatedly, eluting from heaviest to lightest. They are then precipitated as their insoluble oxalates, burned to form the oxides, and then reduced to metals.

Applications

Leo Moser (not to be confused with the mathematician of the same name), son of Ludwig Moser, founder of the Moser Glassworks in what is now Karlovy Vary in the Czech Republic, investigated the use of praseodymium in glass coloration in the late 1920s, yielding a yellow-green glass given the name "Prasemit". However, at that time far cheaper colorants could give a similar color, so Prasemit was not popular, few pieces were made, and examples are now extremely rare. Moser also blended praseodymium with neodymium to produce "Heliolite" glass ("Heliolit" in German), which was more widely accepted. The first enduring commercial use of purified praseodymium, which continues today, is in the form of a yellow-orange "Praseodymium Yellow" stain for ceramics, which is a solid solution in the zircon lattice. This stain has no hint of green in it; by contrast, at sufficiently high loadings, praseodymium glass is distinctly green rather than pure yellow.

Like many other lanthanides, praseodymium's shielded f-orbitals allow for long excited state lifetimes and high luminescence yields. Pr³⁺ as a dopant ion therefore sees many applications in optics and photonics. These include DPSS-lasers, single-mode fiber optical amplifiers, fiber lasers, upconverting nanoparticles as well as activators in red, green, blue, and ultraviolet phosphors. Silicate crystals doped with praseodymium ions have also been used to slow a light pulse down to a few hundred meters per second.

As the lanthanides are so similar, praseodymium can substitute for most other lanthanides without significant loss of function, and indeed many applications such as mischmetal and ferrocerium alloys involve variable mixes of several lanthanides, including small quantities of praseodymium. The following more modern applications involve praseodymium specifically or at least praseodymium in a small subset of the lanthanides:

In combination with neodymium, another rare-earth element, praseodymium is used to create high-power magnets notable for their strength and durability. In general, most alloys of the cerium-group rare earths (lanthanum through samarium) with 3d transition metals give extremely stable magnets that are often used in small equipment, such as motors, printers, watches, headphones, loudspeakers, and magnetic storage.
Praseodymium–nickel intermetallic (PrNi₅) has such a strong magnetocaloric effect that it has allowed scientists to approach within one thousandth of a degree of absolute zero.
As an alloying agent with magnesium to create high-strength metals that are used in aircraft engines; yttrium and neodymium are also viable substitutes.
Praseodymium is present in the rare-earth mixture whose fluoride forms the core of carbon arc lights, which are used in the motion picture industry for studio lighting and projector lights.
Praseodymium compounds give glasses, enamels and ceramics a yellow color.
Praseodymium is a component of didymium glass, which is used to make certain types of welder's and glass blower's goggles.
Praseodymium oxide in solid solution with ceria or ceria-zirconia has been used as an oxidation catalyst.

Due to its role in permanent magnets used for wind turbines, it has been argued that praseodymium will be one of the main objects of geopolitical competition in a world running on renewable energy. However, this perspective has been criticized for failing to recognize that most wind turbines do not use permanent magnets and for underestimating the power of economic incentives for expanded production.

Biological role and precautions

The early lanthanides have been found to be essential to some methanotrophic bacteria living in volcanic mudpots, such as Methylacidiphilum fumariolicum: lanthanum, cerium, praseodymium, and neodymium are about equally effective. Praseodymium is otherwise not known to have a biological role in any other organisms, but it is not very toxic either. Intravenous injection of rare earths into animals has been known to impair liver function, but the main side effects from inhalation of rare-earth oxides in humans come from radioactive thorium and uranium impurities.

Hazards
GHS labelling:
Pictograms
Signal word	Danger
Hazard statements	H250
Precautionary statements	P222, P231, P422
NFPA 704 (fire diamond)	0 4 4